Xiamen Keyuan Plastic Co.,Ltd is one of the professional toughened and reinforced pa66 manufacturers, you can order high quality toughened and reinforced pa66 at good price from our factory.
PA66-product Specifications
Specifications
Toughening organic filler grade PA66 Material
1.Its made from PA66 and flexibilizer (PE—g-MAH（ST-6))
2.High intensity
3.We also can modified plastic materials according to customer's need.
Product name |
PA6/PA66 reinforced with (5%-55%)GF / (10%-50%)toughness /(V0,V1,V2)FR/ UV |
Color |
As required |
Advantage |
Competitive price,high quality,on-time delivery,free sample |
Environment friendly | |
High Heat Resistance,High impact resistance | |
Without any impurity | |
Can be reinforced with the glass fiber/toughness/flame retardant/UV stabilizer | |
Packing |
25kg/bag (also can be customized) |
PA66-Product Properties
Item |
Typical Characteristic |
Testing Standard |
||
KY-NA69FG15 |
KY-NA69FG33 |
KY-NA69FG50 |
||
Density |
1.32g/cm3 |
1.4g/cm3 |
1.5g/cm3 |
ASTM D-792 |
Glass Fiber |
15% |
33% |
50% |
--- |
Molding Shrinkage |
0.4-0.7% |
0.4-0.6% |
0.5-0.7% |
ASTM D-955 |
Tensile Strength |
140MPa |
195MPa |
225MPa |
ASTM D-638 |
Flexural Strength |
268MPa |
288MPa |
310MPa |
ASTM D-790 |
Elongation at break |
5% |
4% |
3% |
ASTM D-638 |
Flexural Modulus |
6300MPa |
6850MPa |
7200MPa |
ASTM D-790 |
Izod Notched Impact Strength |
85J/m |
100J/m |
150J/m |
ASTM D-256 |
Melting Point |
255℃ |
265℃ |
268℃ |
ASTM D-789 |
brittle temperature |
-100℃ |
-105℃ |
-102℃ |
ASTM D-746 |
Heat Deflection Temperature |
230℃(0.5×10^6Pa) |
250℃(0.5×10^6Pa) |
260℃(0.5×10^6Pa) |
ASTM D-648 |
CLTE |
7×10^-5m/m/℃ |
6.5×10^-5m/m/℃ |
6×10^-5m/m/℃ |
ASTM D-696 |
Use temperature | ||||
Processing temperature : 230 - 250 °C | ||||
Mould temperature : 100 - 120 °C | ||||
Back pressure : ca.10 - 15 bar | ||||
Injection speed : medium/high | ||||
Pre-drying : necessary | ||||